Bead wire for tyre
The bead wire is a drawn wire made of high-carbon steel wire rod and plated with bronze on the surface.
Bead wire products of our company can meet the highest requirements of customers in performance indicators such as strength and adhesion,
are widely used in the rubber industry and other wire industries.
Limwell shares can not only meet the international standards of the industry, but also meet the diversified requirements of different customers.
Technical Parameters
Diameter (mm) |
Tolerance (mm ) |
Tensile Strength Level |
Tensile Strength ( MPa ) |
Breaking Force ( N ) |
Elongation (%) |
Torsion (T/360 ) |
Yield Ratio ( % ) |
Straightness (mm/3m ) |
0.89 |
±0.02 |
NT |
≥1900 |
≥1180 |
≥5.0% |
≥50 ( 200d ) |
85% |
≤600 |
±0.02 |
HT |
≥2150 |
≥1340 |
≥5.0% |
≥50 ( 200d ) |
85% |
≤600 |
0.95 |
±0.02 |
NT |
≥1850 |
>1310 |
≥5.0% |
≥50 ( 200d ) |
85% |
≤600 |
±0.02 |
HT |
≥2100 |
≥1490 |
≥5.0% |
≥50 ( 200d ) |
85% |
≤600 |
0.96 |
±0.02 |
NT |
≥1850 |
≥1340 |
≥5.0% |
≥50 ( 200d ) |
85% |
≤600 |
±0.02 |
HT |
≥2100 |
≥1520 |
≥5.0% |
≥50 ( 200d ) |
85% |
≤600 |
1.00 |
±0.02 |
NT |
≥1850 |
≥1450 |
≥5.0% |
≥22( 100d ) |
85% |
≤600 |
±0.02 |
HT |
≥2080 |
≥1630 |
≥5.0% |
≥22( 100d ) |
85% |
≤600 |
1.20 |
±0.02 |
NT |
≥1800 |
≥2035 |
≥5.0% |
≥22( 100d) |
85% |
≤600 |
±0.02 |
HT |
≥2050 |
≥2320 |
≥5.0% |
≥22( 100d) |
85% |
≤600 |
1.26 |
±0.02 |
NT |
≥1790 |
≥2230 |
≥5.0% |
≥22 ( 100d ) |
85% |
≤600 |
±0.02 |
HT |
≥2050 |
≥2555 |
≥5.0% |
≥22( 100d ) |
85% |
≤600 |
1.30 |
±0.02 |
NT |
≥1790 |
≥2375 |
≥5.0% |
≥22 ( 100d ) |
85% |
≤600 |
±0.02 |
HT |
≥2050 |
≥2720 |
≥5.0% |
≥22( 100d ) |
85% |
≤600 |
1.42 |
±0.02 |
NT |
≥1785 |
≥2825 |
≥5.0% |
≥22( 100d ) |
85% |
≤600 |
±0.02 |
HT |
≥2030 |
≥3210 |
≥5.0% |
≥22(100d) |
85% |
≤600 |
1.55 |
±0.02 |
NT |
≥1780 |
≥3360 |
≥5.0% |
≥20 ( 100d ) |
85% |
≤600 |
±0.02 |
HT |
≥2015 |
≥3800 |
≥5.0% |
≥20( 100d ) |
85% |
≤600 |
1.60 |
±0.02 |
NT |
≥1780 |
≥3580 |
≥5.0% |
≥20( 100d ) |
85% |
≤600 |
±0.02 |
HT |
≥2010 |
≥4040 |
≥5.0% |
≥20( 100d) |
85% |
≤600 |
1.65 |
±0.02 |
NT |
≥1780 |
≥3805 |
≥5.0% |
≥20( 100d) |
85% |
≤600 |
1.83 |
±0.03 |
NT |
≥1770 |
≥4650 |
≥5.0% |
≥16( 100d) |
85% |
≤600 |
±0.03 |
HT |
≥2005 |
≥5270 |
≥5.0% |
≥16( 100d) |
85% |
≤600 |
2.00 |
±0.03 |
NT |
≥1680 |
≥5275 |
≥5.0% |
≥16( 100d) |
85% |
≤600 |
±0.03 |
HT |
≥1850 |
≥5810 |
≥5.0% |
≥16( 100d) |
85% |
≤600 |
2.03 |
±0.03 |
NT |
≥1680 |
≥5435 |
≥5.0% |
≥16( 100d) |
85% |
≤600 |
±0.03 |
HT |
≥1850 |
≥5985 |
≥5.0% |
≥16( 100d) |
85% |
≤600 |
2.20 |
±0.03 |
NT |
≥1630 |
≥6190 |
≥5.0% |
≥16( 100d) |
85% |
≤600 |
±0.03 |
HT |
≥1820 |
≥6915 |
≥5.0% |
≥16( 100d) |
85% |
≤600 |