1. Magnesium Oxide specially for Neoperne
SPECIFICATION | |||||
LW-01 | LW-120 | LW-150 | LW-150G | ||
ITEMS | VALUE | ITEMS | VALUE | VALUE | VALUE |
MgO: % ≥ | 93.5 | MgO: % ≥ (850°C constant weight) | 97.5 | 97.5 | 97.5 |
CaO :% ≤ | 0.5 | CaO :% ≤ | 0.5 | 0.5 | 0.5 |
Hydrochloric acid insoluble:% ≤ | 0.2 | Hydrochloric acid insoluble:% ≤ | 0.2 | 0.2 | 0.2 |
Residue greater than 100meshs: % ≤ | nil | Residue greater than 100meshs: % ≤ | nil | nil | nil |
Loss on Ignition: % ≤ | 5 | Loss on Ignition: % ≤ | 10 | 10 | 10 |
Fe: % ≤ | 0.05 | Fe: % ≤ | 0.05 | 0.05 | 0.05 |
Stack Density: (g/ml) ≤ | 0.25 | Stack Density: (g/ml) ≤ | 0.25 | 0.25 | 0.25 |
iodine absorption value: (mgI2/gMgO) ≥ | 120 | 120 | 120 |
SPECIFICATION | |||
LW-02 | LW-150Y | ||
ITEMS | VALUE | ITEMS | VALUE |
MgO: % ≥ | 95 | MgO: % ≥ (850°C constant weight) | 97.5 |
CaO :% ≤ | 1 | CaO :% ≤ | 0.5 |
Hydrochloric acid insoluble:% ≤ | 0.1 | Hydrochloric acid insoluble:% ≤ | 0.1 |
Residue greater than 100meshs: % ≤ | 0.01 | Residue greater than 100meshs: % ≤ | 0.03 |
Loss on Ignition: % ≤ | 3.5 | Loss on Ignition: % ≤ | 10 |
Stack Density: (g/ml) ≤ | 0.2 | Stack Density: (g/ml) ≤ | 0.2 |
iodine absorption value: (mgI2/gMgO) ≥ | 150 |
SPECIFICATION | |||
LW-03 | LW-150P | ||
ITEMS | VALUE | ITEMS | VALUE |
MgO: % ≥ | 93.5 | MgO: % ≥ (850°C constant weight) | 97.5 |
CaO :% ≤ | 1 | CaO :% ≤ | 1 |
Hydrochloric acid insoluble:% ≤ | 0.13 | Hydrochloric acid insoluble:% ≤ | 0.13 |
Residue greater than 100meshs: % ≤ | nil | Residue greater than 100meshs: % ≤ | nil |
Loss on Ignition: % ≤ | 5 | Loss on Ignition: % ≤ | 10 |
Fe: % ≤ | 0.13 | Fe: % ≤ | 0.13 |
Stack Density: (g/ml) ≤ | 0.25 | Stack Density: (g/ml) ≤ | 0.25 |
iodine absorption value: (mgI2/gMgO) ≥ | 150 |
SPECIFICATION | |||||
LW-04 | LW-04D | LW-120 | LW-120C | LW-150C | |
ITEMS | VALUE | VALUE | ITEMS | VALUE | VALUE |
MgO: % ≥ | 93 | 93 | MgO: % ≥ (850°C constant weight) | 97.5 | 97.5 |
CaO :% ≤ | 1 | 1.5 | CaO :% ≤ | 1.5 | 1.5 |
Residue greater than 100meshs: % ≤ | nil | nil | Residue greater than 100meshs: % ≤ | nil | nil |
Loss on Ignition: % ≤ | 5 | 5 | Loss on Ignition: % ≤ | 10 | 10 |
Fe: % ≤ | 0.2 | 0.25 | Fe: % ≤ | 0.2 | 0.2 |
Stack Density: (g/ml) ≤ | 0.2 | 0.2 | Stack Density: (g/ml) ≤ | 0.25 | 0.25 |
iodine absorption value: (mgI2/gMgO) ≥ | 120 | 150 |
SPECIFICATION | |||
LW-05 | LW-150L | ||
ITEMS | VALUE | ITEMS | VALUE |
MgO: % ≥ | 92 | MgO: % ≥ (850°C constant weight) | 97.5 |
CaO :% ≤ | 1.5 | CaO :% ≤ | 1.5 |
Loss on Ignition: % ≤ | 5 | Loss on Ignition: % ≤ | 10 |
Stack Density: (g/ml) ≤ | 0.25 | Stack Density: (g/ml) ≤ | 0.25 |
iodine absorption value: (mgI2/gMgO) ≥ | 150 |
SPECIFICATION | |
LW-06 | |
ITEMS | VALUE |
MgO: % ≥ | 70 |
SPECIFICATION | |||
LW-07 | LW-150S | ||
ITEMS | VALUE | ITEMS | VALUE |
MgO: % ≥ | 93 | MgO: % ≥ (850°C constant weight) | 97.5 |
CaO :% ≤ | 1 | CaO :% ≤ | 1 |
Residue greater than 100meshs: % ≤ | nil | Residue greater than 100meshs: % ≤ | nil |
Loss on Ignition: % ≤ | 5 | Loss on Ignition: % ≤ | 10 |
Fe: % ≤ | 0.15 | Fe: % ≤ | 0.15 |
Stack Density: (g/ml) ≤ | 0.25 | Stack Density: (g/ml) ≤ | 0.25 |
iodine absorption value: (mgI2/gMgO) ≥ | 150 |
SPECIFICATION | |
LW-08 | |
ITEMS | VALUE |
MgO: % ≥ | 95 |
CaO :% ≤ | 0.2 |
Fe: % ≤ | 0.03 |
Residue greater than 100meshs: % ≤ | 0.01 |
Stack Density: (g/ml) ≤ | 0.25 |
Chloride: % ≤ | 0.3 |
Hydrochloric acid insoluble:% ≤ | 0.2 |
Loss on Ignition: % ≤ | 3.5 |
SPECIFICATION | |
LW-09 | |
ITEMS | VALUE |
MgO: % ≥ | 93 |
CaO :% ≤ | 1 |
Stack Density: (g/ml) ≤ | 0.25 |
Residue greater than 100meshs: % ≤ | nil |
SPECIFICATION | |
LW-10 | |
ITEMS | VALUE |
MgO: % ≥ | 96.5 |
CaO :% ≤ | 0.5 |
Fe: % ≤ | 0.05 |
Chloride: % ≤ | 0.03 |
Stack Density: (g/ml) ≤ | 0.15 |
Hydrochloric acid insoluble:% ≤ | 0.2 |
Residue greater than 100meshs: % ≤ | nil |
SPECIFICATION | |
LW-11 | |
ITEMS | VALUE |
MgO: % ≥ | 98 |
CaO :% ≤ | 0.5 |
Residue greater than 100meshs: % ≤ | nil |
Stack Density: (g/ml) ≤ | 0.25 |
Fe:% ≤ | 0.01 |
SPECIFICATION | |
LW-12 | |
ITEMS | VALUE |
MgO: % ≥ | 93 |
CaO :% ≤ | 1.5 |
Stack Density: (g/ml) ≤ | 0.25 |
Residue greater than 100meshs: % ≤ | nil |
SPECIFICATION | |
LW-13 | |
ITEMS | VALUE |
MgO: % ≥ | 93 |
CaO :% ≤ | 2 |
SPECIFICATION | |
LW-14 | |
ITEMS | VALUE |
MgO: % ≥ | 97.5 |
CaO :% ≤ | 0.2 |
Fe: % ≤ | 0.02 |
As: ppm ≤ | 5 |
Stack Density: (g/ml) ≤ | 0.2 |
Hydrochloric acid insoluble:% ≤ | 0.1 |
Residue greater than 100meshs: % ≤ | 0.01 |
Pb: ppm ≤ | 2 |
SPECIFICATION | |
LW-15 | |
ITEMS | VALUE |
MgO: % ≥ | 99 |
CaO :% ≤ | 0.05 |
Whiteness: ≥ | 96.5 |
Stack Density: (g/ml) ≤ | 0.25 |
SPECIFICATION | |
LW-16 | |
ITEMS | VALUE |
MgO: % ≥ | 88 |
CaO :% ≤ | 0.5 |
Stack Density: (g/ml) ≤ | 0.25 |
iodine absorption value: (mgI2/gMgO) ≥ | 150 |
SPECIFICATION | |
LW-17 | |
ITEMS | VALUE |
MgO: % ≥ | 97.5 |
CaO :% ≤ | 0.1 |
Stack Density: (g/ml) ≤ | 0.6 |
SPECIFICATION | |
LW-150F | |
ITEMS | VALUE |
MgO: % ≥ (850°C constant weight) | 97.5 |
CaO :% ≤ | 0.5 |
Fe: % ≤ | 0.03 |
Residue greater than 100meshs: % ≤ | 0.01 |
Stack Density: (g/ml) ≤ | 0.25 |
iodine absorption value: (mgI2/gMgO) ≥ | 150 |
Hydrochloric acid insoluble:% ≤ | 0.1 |
Loss on Ignition: % ≤ | 10 |
SPECIFICATION | ||
LW-101A | LW-101B | |
ITEMS | VALUE | VALUE |
Mg(OH)2: % ≥ | 93 | 93 |
CaO :% ≤ | 0.8 | 0.8 |
Fe: % ≤ | 0.2 | 0.2 |
Moisture: % ≤ | 2 | 2.5 |
Hydrochloric acid insoluble:% ≤ | 2.5 | 2.5 |
Stack Density: (g/ml) ≤ | 0.25 | 0.25 |
Whiteness: ≥ | 93 | 93 |
Average Particle Size (um) | 1.8 | 2.6 |
*DBP Absorption Value: cm2/g ≤ | 0.5 | 0.5 |
SPECIFICATION | |||
LW-102A | LW-102B | LW-102HP | |
ITEMS | VALUE | VALUE | VALUE |
Mg(OH)2: % ≥ | 93 | 93 | 98 |
CaO :% ≤ | 0.5 | 0.8 | 0.005 |
Fe: % ≤ | 0.25 | 0.25 | 0.007 |
Hydrochloric acid insoluble:% ≤ | 2.5 | 2.9 | 0.04 |
Stack Density: (g/ml) ≤ | 0.3 | 0.3 | 0.8 |
Loss on Ignition: % ≤ | 28 | 30 | 25 |
SPECIFICATION | |||||
LW-201A Superior |
LW-201A Qualified |
LW-120 | LW-201B Superior |
LW-201B Qualified |
|
ITEMS | VALUE | VALUE | ITEMS | VALUE | VALUE |
MgO: % ≥ | 92 | 92 | MgO: % ≥ | 88 | 88 |
CaO :% ≤ | 1.5 | 2 | CaO :% ≤ | 1.5 | 2 |
Fe: % ≤ | 0.2 | 0.2 | Fe: % ≤ | 0.2 | 0.2 |
Stack Density: (g/ml) ≤ |
0.25 | 0.25 | Stack Density: (g/ml) ≤ |
0.25 | 0.25 |
Hydrochloric acid insoluble:% ≤ | 1 | 1.2 | Hydrochloric acid insoluble:% ≤ | 1 | 1.2 |
Loss on Ignition: % ≤ | 2 | 2.5 | Loss on Ignition: % ≤ | 8 | 8 |
Average Particle Size (um) | 1.8 | 2.6 | Average Particle Size (um) | 1.8 | 2.6 |
iodine absorption value (mgI2/gMgO) ≥ | 60 | 60 |
SPECIFICATION | |||||
LW-202A Superior | LW-202A Qualified | LW-120 | LW-201B Superior | LW-201B Qualified |
|
ITEMS | VALUE | VALUE | ITEMS | VALUE | VALUE |
MgO: % ≥ | 92 | 92 | MgO: % ≥ | 92 | 92 |
CaO :% ≤ | 0.5 | 1 | CaO :% ≤ | 1.5 | 2 |
Fe: % ≤ | 0.2 | 0.2 | Fe: % ≤ | 0.2 | 0.2 |
Stack Density: (g/ml) ≤ | 0.25 | 0.25 | Stack Density: (g/ml) ≤ |
0.25 | 0.25 |
Hydrochloric acid insoluble:% ≤ | 1 | 1.2 | Hydrochloric acid insoluble:% ≤ | 1 | 1.2 |
Loss on Ignition: % ≤ | 2 | 2.5 | Loss on Ignition: % ≤ | 8 | 8 |
Average Particle Size (um) | 1.8 | 2.6 | Average Particle Size (um) | 1.8 | 2.6 |
iodine absorption value: (mgI2/gMgO) ≥ | 60 | 60 |
Limwell New Material Tech.
In 2013, Shanghai Limwell New Material Tech. Co., Ltd. started the operation in Shanghai, China.